Degradation of Azo Dye Solutions by a Nanocrystalline Fe-Based Alloy and the Adsorption of Their By-Products by Cork.

In this study, the efficiency of mechanically alloyed Fe80Si10B10 in degrading basic red 46 azo dye is investigated. Moreover, the influences of different parameters, such as pH and time, on the elimination of the aromatic derivatives obtained as by-products of the fracture of the azo group are also analyzed. After beginning the reduction to the normal conditions of pH (4.6) and temperature, the experimental findings showed a discoloration of 97.87% after 20 min. The structure and morphology of the nanocrystalline Fe80Si10B10 powder were characterized by SEM and XRD before and after use in the degradation process. The XRD patterns of the Fe-Si-B powder after redox reaction suggest that the valent zero Fe of the alloy is the reducing agent. Powdered cork was then used as a biosorbent for the removal of the by-products generated, resulting in increasing removal percentages from pH 7 (26%) to pH 9 (62%) and a contact time of 120 min. The FTIR spectrum of the cork after adsorption shows a shift of the bands, confirming the interaction with the aromatic amines. The present findings show that metallic powders and natural cork perform well together in removing azo dye solutions and their degradation products.

Study of Structural, Compression, and Soft Magnetic Properties of Fe65Ni28Mn7 Alloy Prepared by Arc Melting, Mechanical Alloying, and Spark Plasma Sintering.

Soft magnetic Fe65Ni28Mn7 (at. %) alloy was successfully synthesized by mechanical alloying and spark plasma sintering (SPS) and, in parallel, the same composition was prepared by arc melting (AM) for comparison. Several SPS conditions were tested. X-ray diffraction and scanning electron microscopy were used to investigate the structure, phase composition, and morphology of the samples. It was found that mechanical alloying produced BCC and FCC supersaturated solid solution after 130 h of milling, with a fine microstructure (i.e., crystallite size of 10 nm). Spark plasma sintering performed at 750 °C and 1000 °C under two pressures of 50 MPa and 75 MPa revealed stable FCC phases. A single FCC phase was observed after the arc melting synthesis. The magnetic properties of milled powders and solids obtained by AM and SPS were investigated. The specimen consolidated by SPS at 1000 °C under the pressure of 50 MPa exhibits soft magnetic behavior (coercivity 0.07 Oe), whereas the mechanically alloyed sample revealed hard magnetic behavior. The specimen consolidated at 750 °C under a pressure of 75 MPa showed a higher compressive strength of 1700 MPa and a Vickers hardness of 425 ± 18 HV. As a result, sintering at 750 °C/75 MPa can be utilized to enhance the mechanical properties, while those sintered at 1000 °C/50 MPa increase magnetic softness.

Nanomaterials as a Sustainable Choice for Treating Wastewater: A Review.

The removal of dyes from textile effluents utilizing advanced wastewater treatment methods with high efficiency and low cost has received substantial attention due to the rise in pollutants in water. The purpose of this work is to give a comprehensive analysis of the different treatments for removing chemical dyes from textile effluents. The capability and potential of conventional treatments for the degradation of dyeing compounds in aqueous media, as well as the influence of multiple parameters, such as the pH solution, initial dye concentration, and adsorbent dose, are presented in this study. This study is an overview of the scientific research literature on this topic, including nanoreductive and nanophotocatalyst processes, as well as nanoadsorbents and nanomembranes. For the purpose of treating sewage, the special properties of nanoparticles are currently being carefully researched. The ability of nanomaterials to remove organic matter, fungus, and viruses from wastewater is another benefit. Nanomaterials are employed in advanced oxidation techniques to clean wastewater. Additionally, because of their small dimensions, nanoparticles have a wide effective area of contact. Due to this, nanoparticles' adsorption and reactivity are powerful. The improvement of nanomaterial technology will be beneficial for the treatment of wastewater. This report also offers a thorough review of the distinctive properties of nanomaterials used in wastewater treatment, as well as their appropriate application and future possibilities. Since only a few types of nanomaterials have been produced, it is also important to focus on their technological feasibility in addition to their economic feasibility. According to this study, nanoparticles (NPs) have a significant adsorption area, efficient chemical reactions, and electrical conductivity that help treat wastewater effectively.

Novel Materials Synthesis by Mechanical Alloying/Milling.

Mechanical alloying (MA) and mechanical milling (MM) are based on the ball milling technique/procedure [...].

Structural, Thermal and Magnetic Analysis of Fe75Co10Nb6B9 and Fe65Co20Nb6B9 Nanostructured Alloys.

Two nanocrystalline ferromagnetic alloys of the Fe-Co-Nb-B system have been produced by mechanical alloying (MA). Their microstructure, thermal behavior and magnetic response were checked by X-ray diffraction (XRD), differential scanning calorimetry (DSC) and vibrating sample magnetometry (VSM). After 80 h of MA, the alloys were nanostructured (bcc-Fe(Co)-rich phase). As the Co content increases, the density of the dislocations decreases. Besides, a higher concentration of Co causes an increase in the activation energy of the crystallization process. The calculated energies, 267 and 332 kJ/mol, are associated to the crystalline growth of the bcc-Fe-rich phase. The Co content of the samples has no effect on the value of the saturation magnetization, whereas the coercivity is lower in the alloy containing less Co. Samples were compacted and heat-treated. Optimal annealing reduces the coercivity by a factor of two. Results were compared with the data of Fe-Nb-B and Fe-Ni-Nb-B alloys.

Investigation of the Critical Behavior, Magnetocaloric Effect and Hyperfine Structure in the Fe72Nb8B20 Powders.

Microstructure as well as magnetic, thermal and magnetocaloric properties of the mechanically alloyed Fe72Nb8B20 powders have been investigated by means of Mössbauer spectrometry, differential scanning calorimetry (DSC), and magnetic measurements. The Mössbauer spectrometry results showed the formation of nanostructured Fe(B) and Fe(Nb) solid solutions, Fe2B boride, and an amorphous phase. The endothermic and exothermic peaks that are observed in the DSC curves might be related to the Curie temperature, and the crystallization of the amorphous phase, respectively. The critical exponent values around the magnetic phase transition of the amorphous phase (TC = 480 K), are deduced from the modified Arrott plots, Kouvel-Fisher curves and critical isotherm examination. The calculated values (ß = 0.457 ± 0.012, γ = 0.863 ± 0.136 and δ = 3.090 ± 0.004) are near to those of the mean field model, revealing a dominating role of magnetic order arising due to long-range ferromagnetic interactions, as the critical exponents are mean-field-like. The maximum entropy change and the refrigerant capacity values are 1.45 J/kg·K and 239 J/kg, respectively, under a magnetic field of 5 T.

Azo-dye degradation by Mn-Al powders.

Manganese-Aluminum powders were recently reported to show high efficiency and fast reaction rates as decolorization materials for azo-dye aqueous solutions. This work presents a detailed study of different aspects of this material. Firstly, the influence of the crystalline phase and the microstructure was studied by comparing the efficiency of powders obtained by different production protocols. Secondly, the decolorization efficiency was investigated on various types of dyes, including real textile wastewater samples. The analysis of the treated water and the particles showed that the main reaction mechanism was the breaking of the azo-dye molecules, although important adsorption on the metallic surface was observed for some colorants. Finally, the reusability of the particles and the reduction of toxicity achieved during the treatments were assessed. The simple production and application methods, the high efficiency and the use of environmentally friendly metallic elements are the main advantages of Manganese-Aluminum powders compared to other high-efficient decolorizing metallic materials.